Abstract:
Introduction. Articular cartilage tissue engineering has a long history of using three-dimensional
matrices seeded with cells of chondrogenic potential. Recent studies show that chondrogenesis is
influenced not only by growth factors, but also by the biochemical microenvironment, including ions
such as Zn²⁺ and Cu²⁺.
Materials and methods: With approval from the Ethics Committee of Nicolae Testemitanu State
University of Medicine and Pharmacy and under a collaboration agreement with the Human Tissue
Bank of the Clinical Hospital of Traumatology and Orthopaedics, articular cartilage was collected from
a donated femoral head, along with processed umbilical-placental complex. Collagen hydrogels (3
mg/ml) were prepared in 24-well plates containing ZnO NPs (<50 nm; Sigma-Aldrich, USA) at 0
(control), 1, 10, 20, 40, 60, 80, and 100 µg/ml (n=4). Their elastic modulus (EM) was measured using
a TX-BLM probe and a TX-700 texture analyzer (Lamy Rheology, France). For viability testing,
human chondrocytes (1×105
cells/ml) were cultured on hydrogels containing 0 (control), 10, 50, or 100
µg/ml ZnO NPs. Resazurin (10 µg/ml; Acros TFS, Belgium) was used as the viability reagent, and
blanks without cells were prepared for each concentration and control group (n=3). Measurements
were performed at 24, 48, and 72 hours after 6 h incubation at 37°C and 5% CO₂. Absorbance was
recorded at 570 and 600 nm using a Synergy H3 spectrophotometer (BioTek, USA).
Results and Conclusions. ZnO NPs concentration markedly affected the mechanical properties of the
hydrogels. Significant differences were found between the control group (470.73 ±38.00 N/m²) and
most ZnO-loaded groups. EM was significantly reduced at 60, 80, and 100 µg/ml ZnO (p <0.05),
whereas at 1, 10, and 20 µg/ml it was significantly higher than in the control group (p <0.05). No
significant difference was observed at 40 µg/ml (p >0.05). The resazurin assay showed a dosedependent effect of ZnO NPs on chondrocyte viability. The highest viability was recorded at 10 µg/ml
ZnO, remaining above 70% over three consecutive days, while higher concentrations caused a marked
decrease in viability (p < 0.05). Therefore, 10 µg/ml ZnO appears to be the most promising
concentration, offering a favorable balance between mechanical strength and cell viability.